EXTERIOR WATER-BASED PAINT KS M 6010 Class 1 Grade 2

usage
Finish coating for exterior walls of alkaline material such as concrete, cement mortar, P.C., plaster, etc.

This paint is an exterior (finishing) water-based paint with excellent alkali resistance, water resistance, weather resistance, and washability resistance, which is made of high-grade acrylic emulsion resin and pigment with excellent weather resistance as the main ingredients.

specification

Paint type
Acrylic emulsion water-based exterior / Top coat
Drying time
Drying time
Category 5℃ 20℃ 30℃
Dry-hard 3 hours 1 hour 40 minutes
Time required for re-coating (min.) 6 hours 3 hours 2 hours
Thinner
Tap water(dilution rate: up to 20%, volume ratio)
Coating Method
Brush, roller, spray coating
Specific gravity
Approx. 1.36(based on white color)
Solid volume ratio
Approx. 37%(based on white color)
Theoretical Coverage
5~7㎡/ℓ/2times
Thickness of dried film
60㎛ (2coats recommended)
Re-coating interval
20℃, sufficient ventilation for a minimum of 3 hours
Color
White, other colors
Gloss
Matte
Storage and preservation
12 months (Dry, cool, and dark place with good ventilation, room temperature 5℃~30℃, humidity less than 80%)

PRODUCT PROPERTIES (PHYSICAL PROPERTY DATA)

KS Standard
It is a KS marked item corresponding to KS M 6010 class 1 grade 2.
Excellent film property
Alkali resistance, washability resistance, water resistance, weather resistance and durability are excellent.

how to use

Surface treatment
1. The material should be sufficiently cured (cured more than 30 days at 20℃)
2. Laitance, dust, oil and other contaminants on the surface must be completely removed.
3. The proper pH of the material must be less than 9, and the percentage of moisture content must be less than 6%.
4. The gaps and grooves on the surface must be filled with exterior water-based putty, and surface adjustment should be made before coating.
5. After the substrate treatment, if necessary, apply 15㎛ D.F.T. of Waterbased Penetrative Sealer DNX-4001 with a roller or a brush to prevent poor adhesion and discoloration defects.
6. For areas where the absorption of the surface is severe, apply once more after at least 3 hours at 20℃.
Coating method
1. Apply twice to get a dry film thickness of 60㎛ with a roller, brush or spray.
2. At this time, apply by diluting with water up to 20%.
3. After 2 coats, the re-coating interval is at least 3 hours after the first top coating at 20℃.